Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 65
Page 176
the corrosion potential of carbon steel were measured electrochemically . While some general interest was shown in pitting , the main concern was Stress Corrosion Cracking ( SCC ) . In ... Carbon Steel Stress Corrosion in High Purity Water.
the corrosion potential of carbon steel were measured electrochemically . While some general interest was shown in pitting , the main concern was Stress Corrosion Cracking ( SCC ) . In ... Carbon Steel Stress Corrosion in High Purity Water.
Page 189
... steel in oxygenated water , neither cyclic potential oscillations nor pitting occurred . Obviously , carbon steel is far more susceptible to pitting in pure water than Type - 304 stainless steel , and with decreasing temperature ...
... steel in oxygenated water , neither cyclic potential oscillations nor pitting occurred . Obviously , carbon steel is far more susceptible to pitting in pure water than Type - 304 stainless steel , and with decreasing temperature ...
Page 224
... carbon steel in water with dissolved oxygen appears to be of little engineering consequence . Failures in SSRT were ductile . Along the gauge length , TGSCC was shallow and associated with high strains . ☆ In general , carbon steel ...
... carbon steel in water with dissolved oxygen appears to be of little engineering consequence . Failures in SSRT were ductile . Along the gauge length , TGSCC was shallow and associated with high strains . ☆ In general , carbon steel ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld