183 / pointed out that the classification of inclusions as active and inactive may be misleading since the activity of inclusions will depend on the potential and chloride - ion content of the system . The difference between active and ...
183 / pointed out that the classification of inclusions as active and inactive may be misleading since the activity of inclusions will depend on the potential and chloride - ion content of the system . The difference between active and ...
Page 151
If the anodic polarization curve of the metal exhibits an unusually active value of passivation potential such that this potential is more active than the reversible hydrogen electrode potential then passivity can be achieved by the ...
If the anodic polarization curve of the metal exhibits an unusually active value of passivation potential such that this potential is more active than the reversible hydrogen electrode potential then passivity can be achieved by the ...
Page 176
The potential was observed to fall to around -300 to -320 mV ( sce ) which is clearly well within the range of active potentials associated with corrosion . The results are apparently contradictory to those of Tomashov and the important ...
The potential was observed to fall to around -300 to -320 mV ( sce ) which is clearly well within the range of active potentials associated with corrosion . The results are apparently contradictory to those of Tomashov and the important ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld