Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 81
Page 184
... Figure 2 , fabricated from the same material as the tensile specimen , was also installed . The SSRT facility , Figure 6 , permitted the continuous elongation of a specimen in a controlled environment , while corrosion potentials of the ...
... Figure 2 , fabricated from the same material as the tensile specimen , was also installed . The SSRT facility , Figure 6 , permitted the continuous elongation of a specimen in a controlled environment , while corrosion potentials of the ...
Page 207
The metallography ( Figure 25 ) shows severe plastic deformation , and the crack propagated only a distance of 0.015 in . before blunting . Shallow pits also occurred as shown in Figure 25. As the temperature was reduced , the depth of ...
The metallography ( Figure 25 ) shows severe plastic deformation , and the crack propagated only a distance of 0.015 in . before blunting . Shallow pits also occurred as shown in Figure 25. As the temperature was reduced , the depth of ...
Page 298
... ( Figure 18 ) are markedly higher than those in pure HCl ( Figure 2 ) . Dissolved oxygen is not a strong enough oxidizer to passivate alloy C - 276 , and a decrease in corrosion rates is observed when oxygen is removed from HCl ( Figure ...
... ( Figure 18 ) are markedly higher than those in pure HCl ( Figure 2 ) . Dissolved oxygen is not a strong enough oxidizer to passivate alloy C - 276 , and a decrease in corrosion rates is observed when oxygen is removed from HCl ( Figure ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld