... element . However , the phosphorus level shown in Fig . 5 is too small for such analysis to be made , and this is not surprising considering that the origin of the phosphorus is the confinement of a segregated grain boundary . In order ...
... element . However , the phosphorus level shown in Fig . 5 is too small for such analysis to be made , and this is not surprising considering that the origin of the phosphorus is the confinement of a segregated grain boundary . In order ...
Page 171
... elements did not reproduce the pitting resistance of the same elements when bulk alloyed in the steel . This implies that the beneficial influence of the bulk alloyed element is in some way related to its influence on reducing the ...
... elements did not reproduce the pitting resistance of the same elements when bulk alloyed in the steel . This implies that the beneficial influence of the bulk alloyed element is in some way related to its influence on reducing the ...
Page 173
... element has on the pitting propensity of stainless steels in chloride containing environments . The influence of Si and V implants were also investigated since , whilst these elements were not expected to affect the corrosion behaviour ...
... element has on the pitting propensity of stainless steels in chloride containing environments . The influence of Si and V implants were also investigated since , whilst these elements were not expected to affect the corrosion behaviour ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld