... Weight loss methods / 1-3 / require removal of corrosion products and are cumbersome . Weight gain determination of specimen is an improvement over the former , but the selective nature of corrosion and the dissolved products can lead ...
... Weight loss methods / 1-3 / require removal of corrosion products and are cumbersome . Weight gain determination of specimen is an improvement over the former , but the selective nature of corrosion and the dissolved products can lead ...
Page 251
... weight changes or pit depth measurements are likewise non - reliable indicators . While some rust was physically removed upon solvent dissolution of the coating at the test conclusion , this could be drawn from a number of factors not ...
... weight changes or pit depth measurements are likewise non - reliable indicators . While some rust was physically removed upon solvent dissolution of the coating at the test conclusion , this could be drawn from a number of factors not ...
Page 408
... weight loss of the samples containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the ...
... weight loss of the samples containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium