Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 24
Page 76
... thickness surpasses 1 μ . In deposition from acidic solutions higher thicknesses can be achieved while maintaining still good morphological properties of the deposits . However , the composition and therefore the colour of these ...
... thickness surpasses 1 μ . In deposition from acidic solutions higher thicknesses can be achieved while maintaining still good morphological properties of the deposits . However , the composition and therefore the colour of these ...
Page 77
... thicknesses depending on the application . Examples of such applications and the relevant thicknesses are summarized in Table 1 . TABLE 1 : Examples of applications of decorative coatings and their thickness 1 . Gilding of souvenirs 2 ...
... thicknesses depending on the application . Examples of such applications and the relevant thicknesses are summarized in Table 1 . TABLE 1 : Examples of applications of decorative coatings and their thickness 1 . Gilding of souvenirs 2 ...
Page 347
... thickness with a high frequency tester . Valves cast in the first melt were measured and it was discovered that the wall thickness in the suspect areas was considerably thinner than desired - under 7 mm instead of the designed 12.5 + mm ...
... thickness with a high frequency tester . Valves cast in the first melt were measured and it was discovered that the wall thickness in the suspect areas was considerably thinner than desired - under 7 mm instead of the designed 12.5 + mm ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium