Page 334
Previously used cast , mild steel valves , lined with alloy HV 9 , failed by stress corrosion in periods of one week to several months at the welds . Proper stress corrosion testing requires the use of fracture mechanics specimens and ...
Previously used cast , mild steel valves , lined with alloy HV 9 , failed by stress corrosion in periods of one week to several months at the welds . Proper stress corrosion testing requires the use of fracture mechanics specimens and ...
Page 388
There is a threshold stress below which cracking does not occur in an extended period of time . Lowering stresses below the threshold value can prevent SCC . This may be done by annealing to reduce residual stresses , thickening the ...
There is a threshold stress below which cracking does not occur in an extended period of time . Lowering stresses below the threshold value can prevent SCC . This may be done by annealing to reduce residual stresses , thickening the ...
Page 398
Susceptibility of Zirconium in 90 % Nitric Acid mechanism for the SCC of zirconium in HNO3 is stress assisted local anodic dissolution rather than hydrogen embrittlement . Other evidence supporting this mechanism includes : 1.
Susceptibility of Zirconium in 90 % Nitric Acid mechanism for the SCC of zirconium in HNO3 is stress assisted local anodic dissolution rather than hydrogen embrittlement . Other evidence supporting this mechanism includes : 1.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone