Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 63
Page 403
... stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were evolved between the ...
... stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were evolved between the ...
Page 404
... stainless steel in H2SO4 . 3. EXPERIMENTAL METHODS The studies were carried out on the following types of specimens : a ) hot pressed 316 stainless steel / 2 / ; b ) Hot pressed sintered stainless steel containing Cu , Ni and Pd ...
... stainless steel in H2SO4 . 3. EXPERIMENTAL METHODS The studies were carried out on the following types of specimens : a ) hot pressed 316 stainless steel / 2 / ; b ) Hot pressed sintered stainless steel containing Cu , Ni and Pd ...
Page 410
... stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates high passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed ...
... stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates high passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium