INTRODUCTION > The environmental behaviour of hot pressed , sintered austenitic stainless steel in H2SO4 was reported previously / 2 / . It was concluded that the low corrosion resistance of hot pressed stainless steel as compared to ...
INTRODUCTION > The environmental behaviour of hot pressed , sintered austenitic stainless steel in H2SO4 was reported previously / 2 / . It was concluded that the low corrosion resistance of hot pressed stainless steel as compared to ...
Page 404
Behavior of Sintered Stainless Steel concluded that high Pd content ( higher than 1Wt % ) depresses the anodic passivation and enhance the cathodic activity on the exposed surface , due to cathodic depolarization effect .
Behavior of Sintered Stainless Steel concluded that high Pd content ( higher than 1Wt % ) depresses the anodic passivation and enhance the cathodic activity on the exposed surface , due to cathodic depolarization effect .
Page 410
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone