... specimens of as - received and 400 ° C - steam treated materials showed a higher resistance to SCC in 90 % HNO3 than longitudinal specimens as given in Table 3. Transverse specimens of heat treated materials became more susceptible to ...
... specimens of as - received and 400 ° C - steam treated materials showed a higher resistance to SCC in 90 % HNO3 than longitudinal specimens as given in Table 3. Transverse specimens of heat treated materials became more susceptible to ...
Page 396
... specimens show better mechanical pro- perties in HF - containing 90 % HNO3 than transverse specimens as illustrated in Table 6. Apparently , the addition of HF into 90 % HNO3 lowers the potentials of longitudinal specimens more than ...
... specimens show better mechanical pro- perties in HF - containing 90 % HNO3 than transverse specimens as illustrated in Table 6. Apparently , the addition of HF into 90 % HNO3 lowers the potentials of longitudinal specimens more than ...
Page 404
... specimens : a ) hot pressed 316 stainless steel / 2 / ; b ) Hot pressed sintered stainless steel containing Cu , Ni and Pd additions ( Wt % ) of : 0.1-10 . The specimens were obtained by the following procedure : 3g of powder were hot ...
... specimens : a ) hot pressed 316 stainless steel / 2 / ; b ) Hot pressed sintered stainless steel containing Cu , Ni and Pd additions ( Wt % ) of : 0.1-10 . The specimens were obtained by the following procedure : 3g of powder were hot ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium