... slurry vessel or can be held in a process stream , in which case the vessel and its stirrer are not used . The ... slurry ( 1 , 2 ) . A cross - shaped , rigid polypropylene abrader ( 6 ) or a soft rubber wiper is attached to the base of ...
... slurry vessel or can be held in a process stream , in which case the vessel and its stirrer are not used . The ... slurry ( 1 , 2 ) . A cross - shaped , rigid polypropylene abrader ( 6 ) or a soft rubber wiper is attached to the base of ...
Page 363
... Slurry I. Runs Made to Determine the Effect of Environmental Chloride Content : 10,000 ppm C1 , 30 days , slurry pH 6.5 at 52 to 57 ° C Run 1 2 3 50,000 ppm C1 , 50,000 ppm C1 19 days , slurry pH 6.5 at 52 to 57 ° C 30 days , slurry pH ...
... Slurry I. Runs Made to Determine the Effect of Environmental Chloride Content : 10,000 ppm C1 , 30 days , slurry pH 6.5 at 52 to 57 ° C Run 1 2 3 50,000 ppm C1 , 50,000 ppm C1 19 days , slurry pH 6.5 at 52 to 57 ° C 30 days , slurry pH ...
Page 383
... slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with ...
... slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium