Page 338
... slurry vessel or can be held in a process stream , in which case the vessel and its stirrer are not used . The ... slurry ( 1 , 2 ) . A cross - shaped , rigid polypropylene abrader ( 6 ) or a soft rubber wiper is attached to the ...
... slurry vessel or can be held in a process stream , in which case the vessel and its stirrer are not used . The ... slurry ( 1 , 2 ) . A cross - shaped , rigid polypropylene abrader ( 6 ) or a soft rubber wiper is attached to the ...
Page 363
... slurry pH 6.5 at 52 to 57 ° C 3 50,000 ppm Cl , 30 days , slurry pH 6.5 at 50 to 57 ° C 4 100,000 ppm Cl 30 days , slurry pH 6.5 at 50 to 57 ° C , Slurry Cl was added as NaCl . Sulfur dioxide gas 800 mg / L . Excess oxygen in flue gas ...
... slurry pH 6.5 at 52 to 57 ° C 3 50,000 ppm Cl , 30 days , slurry pH 6.5 at 50 to 57 ° C 4 100,000 ppm Cl 30 days , slurry pH 6.5 at 50 to 57 ° C , Slurry Cl was added as NaCl . Sulfur dioxide gas 800 mg / L . Excess oxygen in flue gas ...
Page 383
... slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with ...
... slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion rate corrosion resistance current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion stress corrosion cracking structure substrate Surface Pit Depth Table techniques Technology temperature welding zirconium zirconium in 90 ΔΕ