Page 403
... sintered stainless steel . As a result sintered stainless steel is severely corroded in H2SO4 while a wrought plate or cast austenitic stainless steel remain passive in this environment . Improved corrosion resistance of cast metals ...
... sintered stainless steel . As a result sintered stainless steel is severely corroded in H2SO4 while a wrought plate or cast austenitic stainless steel remain passive in this environment . Improved corrosion resistance of cast metals ...
Page 404
... sintered at a temperature of 1150 ° C for 2h or 48h in vacuum lower than 1 m bar . After sintering at 1150 ° C , the specimens were water quenched . The hot pressing apparatus is described elsewhere / 3 / . The specimens obtained in ...
... sintered at a temperature of 1150 ° C for 2h or 48h in vacuum lower than 1 m bar . After sintering at 1150 ° C , the specimens were water quenched . The hot pressing apparatus is described elsewhere / 3 / . The specimens obtained in ...
Page 410
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium