Page 89
... shows the effect of ton on porosity . The porosity is reduced with decrease of ton . b d a ro C Fig . 4 . Effect of ton on porosity from left to right ( x 3000 ) a . ton = 5 msec ; b . 25 msec ; c . 1 msec ; d . 2.5 sec . Another aspect ...
... shows the effect of ton on porosity . The porosity is reduced with decrease of ton . b d a ro C Fig . 4 . Effect of ton on porosity from left to right ( x 3000 ) a . ton = 5 msec ; b . 25 msec ; c . 1 msec ; d . 2.5 sec . Another aspect ...
Page 276
... shows that the corrosion rate is given by the relation Ig = A / Rp , which , however , should not be confused with ... show how useful the polarization resistance may be for an evaluation of uniform corrosion rate of a metal . 3. THEORY ...
... shows that the corrosion rate is given by the relation Ig = A / Rp , which , however , should not be confused with ... show how useful the polarization resistance may be for an evaluation of uniform corrosion rate of a metal . 3. THEORY ...
Page 396
... shows that the addition of 200ppm HF with or without 800ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800ppm zirconium sponge only produced little changes . The addition of zirconium ...
... shows that the addition of 200ppm HF with or without 800ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800ppm zirconium sponge only produced little changes . The addition of zirconium ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium