Typical test racks are shown in Figures 1 , 2 and 3 , and field test results are shown in Table 2 . Table 1. Alloy ranking from laboratory tests ( scale 1 185 S. Marchand , A. Asphahani and D. Carlson Corrosion Reviews.
Typical test racks are shown in Figures 1 , 2 and 3 , and field test results are shown in Table 2 . Table 1. Alloy ranking from laboratory tests ( scale 1 185 S. Marchand , A. Asphahani and D. Carlson Corrosion Reviews.
Page 209
An abbreviated version of the logic diagram is shown in Figure 2. By developing the rules in a manner which was consistent with the logic diagram , as distinct from an ad hoc approach , it was ...
An abbreviated version of the logic diagram is shown in Figure 2. By developing the rules in a manner which was consistent with the logic diagram , as distinct from an ad hoc approach , it was ...
Page 396
The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility .
The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone