Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 31
Page 406
... samples after exposure to IN H2SO4 solution for 150h . After the exposure to the corrosive environment , the polarization behaviour of samples containing various concentrations of Cu becomes similar . XPS measurements show that surface ...
... samples after exposure to IN H2SO4 solution for 150h . After the exposure to the corrosive environment , the polarization behaviour of samples containing various concentrations of Cu becomes similar . XPS measurements show that surface ...
Page 408
... samples sintered for 2h tested in IN H2SO4 solution are presented in Fig . 4. Samples containing Ni exhibit clear anodic active - passive transition . The passivation current density decreases by two order of magnitude by increasing the ...
... samples sintered for 2h tested in IN H2SO4 solution are presented in Fig . 4. Samples containing Ni exhibit clear anodic active - passive transition . The passivation current density decreases by two order of magnitude by increasing the ...
Page 410
... samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples ...
... samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium