It can be assumed that as a result of this process the steady state Cu surface concentration of different samples become similar . Potentiodynamic polarization measurements show irregular polarization behaviour related to the surface ...
It can be assumed that as a result of this process the steady state Cu surface concentration of different samples become similar . Potentiodynamic polarization measurements show irregular polarization behaviour related to the surface ...
Page 408
The weight loss of the samples containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) .
The weight loss of the samples containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) .
Page 410
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in INH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone