... runs . II . Runs Made to Determine the Effect of Environmental Fluoride Content : Runs 5 , 6 , and 7 were 50,000 ppm C1 , 30 days , slurry pH 5 to 5.5 at 55 to 59 ° C - In Run 5 , the C1 was added as calcium chloride . In Runs 6 and 7 ...
... runs . II . Runs Made to Determine the Effect of Environmental Fluoride Content : Runs 5 , 6 , and 7 were 50,000 ppm C1 , 30 days , slurry pH 5 to 5.5 at 55 to 59 ° C - In Run 5 , the C1 was added as calcium chloride . In Runs 6 and 7 ...
Page 373
... runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least squares fit lines for each alloy indicate the maximum ...
... runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least squares fit lines for each alloy indicate the maximum ...
Page 378
... Run 5 Run 5 ( ails ) 6 7 Run 5 Maximum Crevice Pit Depth ( mils ) 6 7 SS316 4 16 44 83 11 904L 10 38 76 138 26 G 8 68 118 175 36 G - 3 3 24 35 7 28 ¥ ནྡྷུ་ྲཌ 42 27 75 71 105 147 17 39 625 1 3 24 4 10 43 48 Note : Runs 5 to 7 varied the ...
... Run 5 Run 5 ( ails ) 6 7 Run 5 Maximum Crevice Pit Depth ( mils ) 6 7 SS316 4 16 44 83 11 904L 10 38 76 138 26 G 8 68 118 175 36 G - 3 3 24 35 7 28 ¥ ནྡྷུ་ྲཌ 42 27 75 71 105 147 17 39 625 1 3 24 4 10 43 48 Note : Runs 5 to 7 varied the ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium