Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 16
Page 98
... passive film on iron consists of an outer layer of ferric oxide and an inner layer of mixed ferric and ferrous oxides near the substrate . This passive film breaks down spontaneously by reductive dissolution in aqueous solutions or by ...
... passive film on iron consists of an outer layer of ferric oxide and an inner layer of mixed ferric and ferrous oxides near the substrate . This passive film breaks down spontaneously by reductive dissolution in aqueous solutions or by ...
Page 393
... passive behaviors , since activity promotes general corrosion , while passivity will significantly retard any corrosion process . Hence SCC is likely to occur in the active - passive transitional areas of a polarization curve / 20 ...
... passive behaviors , since activity promotes general corrosion , while passivity will significantly retard any corrosion process . Hence SCC is likely to occur in the active - passive transitional areas of a polarization curve / 20 ...
Page 410
... passive during the immersion test and the open circuit potential was in the passive range . From the presented results and other reports / 3 , 14 / it can be concluded that passive behaviour could be expected in sintered stainless steel ...
... passive during the immersion test and the open circuit potential was in the passive range . From the presented results and other reports / 3 , 14 / it can be concluded that passive behaviour could be expected in sintered stainless steel ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium