Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 19
Page 99
... passivation . If the inhibitor's own reduction is too slow for passivation as in the case of MnO4 or WO4 , it reduces the required current density to a degree that dissolved oxygen or some other oxidizing agent present can promote ...
... passivation . If the inhibitor's own reduction is too slow for passivation as in the case of MnO4 or WO4 , it reduces the required current density to a degree that dissolved oxygen or some other oxidizing agent present can promote ...
Page 410
... passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed after 48h of sintering in samples containing Ni . Lower critical and passivation current densities were observed ...
... passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed after 48h of sintering in samples containing Ni . Lower critical and passivation current densities were observed ...
Page 414
... passivation processes of sintered stainless steel . 3. Samples containing 0.1-0.5 Wt % Pd exhibit clear and effective anodic passivation , while in samples with Pd content higher than 1 wt % effective anodic passivation is not observed ...
... passivation processes of sintered stainless steel . 3. Samples containing 0.1-0.5 Wt % Pd exhibit clear and effective anodic passivation , while in samples with Pd content higher than 1 wt % effective anodic passivation is not observed ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium