Page 76
... obtained by pulsed current vs. direct current was made on thin deposits obtained from alkaline and neutral solutions . No significant differences were found in wear resistance , hardness and contact resistance . However , a significant ...
... obtained by pulsed current vs. direct current was made on thin deposits obtained from alkaline and neutral solutions . No significant differences were found in wear resistance , hardness and contact resistance . However , a significant ...
Page 85
The results obtained in this study are summarized in Table 10 . TABLE 10 : Results obtained in deposition from neutral electrolyte Morphology : Wear resistance : Porosity : Hardness : Deposition rate : Contamination : Differences in ...
The results obtained in this study are summarized in Table 10 . TABLE 10 : Results obtained in deposition from neutral electrolyte Morphology : Wear resistance : Porosity : Hardness : Deposition rate : Contamination : Differences in ...
Page 91
The results are manifested in Figs . 5 , 6. Dendritic deposits are obtained in d.c. plating with high chemical inhomogeneity in the dendrites . Smooth and homogeneous deposits are obtained at a double deposition rate at optimal p.c. ...
The results are manifested in Figs . 5 , 6. Dendritic deposits are obtained in d.c. plating with high chemical inhomogeneity in the dendrites . Smooth and homogeneous deposits are obtained at a double deposition rate at optimal p.c. ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium