Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 24
Page 160
... lines , AND one line is at 45 ° , AND one line is at 135 ° , AND they are of equal length , a full space , AND they intersect at the center of the picture , THEN the letter is an ' x ' . The antecendent ( IF clause ) can be as complex ...
... lines , AND one line is at 45 ° , AND one line is at 135 ° , AND they are of equal length , a full space , AND they intersect at the center of the picture , THEN the letter is an ' x ' . The antecendent ( IF clause ) can be as complex ...
Page 164
... lines and arcs , and give its output to a word - identifier . If it fails to identify a letter , it might ask the line - arc decomposer to try again for other lines . Similarly , if the word generator decides a letter cannot be right ...
... lines and arcs , and give its output to a word - identifier . If it fails to identify a letter , it might ask the line - arc decomposer to try again for other lines . Similarly , if the word generator decides a letter cannot be right ...
Page 373
... lines for each alloy indicate the maximum crevice pit depth also increased with increasing environmental chloride content . While SS304 did not significantly crevice corrode , it did suffer severe general corrosion . See Figure 2 . Also ...
... lines for each alloy indicate the maximum crevice pit depth also increased with increasing environmental chloride content . While SS304 did not significantly crevice corrode , it did suffer severe general corrosion . See Figure 2 . Also ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium