Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 8
Page 360
... initiation increased . 1. INTRODUCTION A model SO2 scrubber at the LaQue Center for Corrosion Technology , Inc. ( LCCT ) has been used to characterize the corrosion behavior of austenitic stainless steels and nickel base alloys exposed ...
... initiation increased . 1. INTRODUCTION A model SO2 scrubber at the LaQue Center for Corrosion Technology , Inc. ( LCCT ) has been used to characterize the corrosion behavior of austenitic stainless steels and nickel base alloys exposed ...
Page 389
... initiation of cracks . Results of U - bend tests of a zirconium - 1.5 % tin alloy in 90 % HNO3 showed that surface scratches serve as sites for crack initiation and lowered time - to - failure / 9 / . Improved surface quality will ...
... initiation of cracks . Results of U - bend tests of a zirconium - 1.5 % tin alloy in 90 % HNO3 showed that surface scratches serve as sites for crack initiation and lowered time - to - failure / 9 / . Improved surface quality will ...
Page 393
... initiation . Heat treatments could have improved zirconium's SCC resistance with respect to the difficulties of crack initiation . The U - bend test method would be a good technique to use in evaluating this possibility . Moreover ...
... initiation . Heat treatments could have improved zirconium's SCC resistance with respect to the difficulties of crack initiation . The U - bend test method would be a good technique to use in evaluating this possibility . Moreover ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium