Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 55
Page 360
... environmental effects on localized corrosion propagation of each alloy . Increasing environmental chloride and / or fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in ...
... environmental effects on localized corrosion propagation of each alloy . Increasing environmental chloride and / or fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in ...
Page 373
... environmental chloride content , major attack only occurred in the 100,000 ppm chloride environment . See run 4 in Table 6. The reason for the unexpected behavior of alloy 625 is not clearly discernible . 3.1 Effect of Environmental ...
... environmental chloride content , major attack only occurred in the 100,000 ppm chloride environment . See run 4 in Table 6. The reason for the unexpected behavior of alloy 625 is not clearly discernible . 3.1 Effect of Environmental ...
Page 406
... environment surface segregation of Cu takes place . It can be assumed that as a result of this process the steady state Cu surface concentration of different samples become similar . Potentiodynamic polarization measurements show ...
... environment surface segregation of Cu takes place . It can be assumed that as a result of this process the steady state Cu surface concentration of different samples become similar . Potentiodynamic polarization measurements show ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium