Page 76
... deposits obtained by pulse plating were studied . It was found that in these , relatively thick deposits , pulse plating is advantageous . Higher plating rates and lower porosity were obtained as compared to these characteristics of ...
... deposits obtained by pulse plating were studied . It was found that in these , relatively thick deposits , pulse plating is advantageous . Higher plating rates and lower porosity were obtained as compared to these characteristics of ...
Page 78
... deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu → red Ni → white Ag → green Zn → green Cu + Ag → yellow Cd → green Most decorative deposits are obtained from solutions which differ from ...
... deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu → red Ni → white Ag → green Zn → green Cu + Ag → yellow Cd → green Most decorative deposits are obtained from solutions which differ from ...
Page 85
... deposits was studied by Auger spectrography for deposits obtained by p.c. and on deposits obtained by d.c. in two commercial solutions . While no effect of the plating regime was found , carbon contamination of the surface was detected ...
... deposits was studied by Auger spectrography for deposits obtained by p.c. and on deposits obtained by d.c. in two commercial solutions . While no effect of the plating regime was found , carbon contamination of the surface was detected ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium