Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 28
Page 381
... cracking in the wet - dry zone / 5 / . 4. SUMMARY These data provide useful guidelines for application of various nickel alloys and stainless steels in actual utility SO2 scrubber applications . For example , alloys 625 and C - 276 in ...
... cracking in the wet - dry zone / 5 / . 4. SUMMARY These data provide useful guidelines for application of various nickel alloys and stainless steels in actual utility SO2 scrubber applications . For example , alloys 625 and C - 276 in ...
Page 396
... cracking , SCC should be observed within a certain strain - rate range . When the cracking susceptibility continues to increase with decreasing strain rate , hydrogen embrittlement is likely to be the cause of cracking . The longer the ...
... cracking , SCC should be observed within a certain strain - rate range . When the cracking susceptibility continues to increase with decreasing strain rate , hydrogen embrittlement is likely to be the cause of cracking . The longer the ...
Page 398
... cracking has been observed is much more noble than the hydrogen reversible potential in this solution . 2. A small ... cracking 398 Vol . 7 , No. 4 , 1987 Factors Affecting the Stress Corrosion Cracking.
... cracking has been observed is much more noble than the hydrogen reversible potential in this solution . 2. A small ... cracking 398 Vol . 7 , No. 4 , 1987 Factors Affecting the Stress Corrosion Cracking.
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium