Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 51
Page 405
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to -250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than 200mV ( SCE ) ...
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to -250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than 200mV ( SCE ) ...
Page 408
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
Page 410
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium