Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 17
Page 100
... chromate ( containing Cr - 51 ) , an adherent , adsorbed or ion exchanged monolayer of chromate ions forms immediately / 37-39 , 41 , 45 / . On the other hand the benzoate ion is taken up to the extent of only 6-10 % of a monolayer / 33 ...
... chromate ( containing Cr - 51 ) , an adherent , adsorbed or ion exchanged monolayer of chromate ions forms immediately / 37-39 , 41 , 45 / . On the other hand the benzoate ion is taken up to the extent of only 6-10 % of a monolayer / 33 ...
Page 103
... chromate in solution . It did not lead to an increased consumption since the amount of chromate consumed in protecting a metal surface decreased as the concentration of chromate increased . Although the concentration required to inhibit ...
... chromate in solution . It did not lead to an increased consumption since the amount of chromate consumed in protecting a metal surface decreased as the concentration of chromate increased . Although the concentration required to inhibit ...
Page 104
... chromate was found to be more susceptible to chloride than to sulphate at all chromate concentrations while nitrate became relatively more aggressive in comparison with CI and SO as the chromate concentration increased ( Fig . 4 ) . The ...
... chromate was found to be more susceptible to chloride than to sulphate at all chromate concentrations while nitrate became relatively more aggressive in comparison with CI and SO as the chromate concentration increased ( Fig . 4 ) . The ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium