Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 29
Page 104
... chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with increase of either salt concentration or temperature . Darrin also ...
... chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with increase of either salt concentration or temperature . Darrin also ...
Page 372
... Chloride Content ( ppm x 1000 ) Figure 2 - Corrosion rate vs. environmental chloride content for alloys evaluated in outlet ducting Zone F in runs 1 to 4. 1 mpy = 0.025 mm / y . 150- 125- 100 75- 50- 25- Max . Bold Surface Pit Depth ...
... Chloride Content ( ppm x 1000 ) Figure 2 - Corrosion rate vs. environmental chloride content for alloys evaluated in outlet ducting Zone F in runs 1 to 4. 1 mpy = 0.025 mm / y . 150- 125- 100 75- 50- 25- Max . Bold Surface Pit Depth ...
Page 383
... chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy ...
... chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium