Effect of Aggressive Ions on Inhibition The effect of aggressive ions like chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with ...
Effect of Aggressive Ions on Inhibition The effect of aggressive ions like chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with ...
Page 372
507 40SS304 30Corrosion Rate ( mpy ) 20SS316 10904L C.4'625 1 2 3 Environmental Chloride Content ( ppm x 1000 ) Figure 2 - Corrosion rate vs. environmental chloride content for alloys evaluated in outlet ducting Zone F in runs I to 4.
507 40SS304 30Corrosion Rate ( mpy ) 20SS316 10904L C.4'625 1 2 3 Environmental Chloride Content ( ppm x 1000 ) Figure 2 - Corrosion rate vs. environmental chloride content for alloys evaluated in outlet ducting Zone F in runs I to 4.
Page 383
Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing ...
Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone