Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 13
Page 42
... aluminum oxide films on the aluminum surface . The net effect was initial wetting , followed by dewetting and restricted spreading of the solder . When the copper preplating was made substantially thicker , complete dissolution of the ...
... aluminum oxide films on the aluminum surface . The net effect was initial wetting , followed by dewetting and restricted spreading of the solder . When the copper preplating was made substantially thicker , complete dissolution of the ...
Page 44
... aluminum extrusion is illustrated in Fig . 6. The soldered assemblies , with lengths varying between 30 cm and 1 m , are to be used as heat pipes for the thermal regulation of electronic devices for instance , in satellites . Fig . 6 ...
... aluminum extrusion is illustrated in Fig . 6. The soldered assemblies , with lengths varying between 30 cm and 1 m , are to be used as heat pipes for the thermal regulation of electronic devices for instance , in satellites . Fig . 6 ...
Page 45
... aluminum and stainless steels are being notorious examples of hard - to - join metals , several precoating combinations were evaluated . The finally adopted method consisted of Ni - plating the stainless steel tube and Ni + tin plating ...
... aluminum and stainless steels are being notorious examples of hard - to - join metals , several precoating combinations were evaluated . The finally adopted method consisted of Ni - plating the stainless steel tube and Ni + tin plating ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium