Page 396
Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800 ppm zirconium sponge only produced little changes .
Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800 ppm zirconium sponge only produced little changes .
Page 403
Sn addition improves the corrosion resistance of sintered austenitic stainless steel 13 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
Sn addition improves the corrosion resistance of sintered austenitic stainless steel 13 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
Page 410
The Pd addition up to 5Wt % reacts with the austenitic matrix to form a solid solution . X - Ray diffraction revealed the existence of carbide phases such as M23Co and M3C , after the sintering process . Pd containing phases were not ...
The Pd addition up to 5Wt % reacts with the austenitic matrix to form a solid solution . X - Ray diffraction revealed the existence of carbide phases such as M23Co and M3C , after the sintering process . Pd containing phases were not ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone