Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 30
Page 373
... Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least squares fit lines for each alloy indicate the maximum crevice pit depth also ...
... Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least squares fit lines for each alloy indicate the maximum crevice pit depth also ...
Page 381
... Zone F for 30 to 90 days in run 8. 1 mil = 0.025 mm . Time in the outlet ducting during run 8. As with Zone B , no overall effect of exposure time on alloy pitting and crevice corrosion could be clearly discerned . Alloys ranked as to ...
... Zone F for 30 to 90 days in run 8. 1 mil = 0.025 mm . Time in the outlet ducting during run 8. As with Zone B , no overall effect of exposure time on alloy pitting and crevice corrosion could be clearly discerned . Alloys ranked as to ...
Page 383
... zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased ...
... zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium