Page 373
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
Page 381
Crevice Pit Depth ( mils ) 754 -625 501 -904L SS317LM 25 SS316 -C - 276 20 30 40 50 60 70 80 90 100 Immersion Time ( days ) Figure 10 - Maximum crevice pit depth vs. exposure time for alloys evaluated in the outlet ducting Zone F for 30 ...
Crevice Pit Depth ( mils ) 754 -625 501 -904L SS317LM 25 SS316 -C - 276 20 30 40 50 60 70 80 90 100 Immersion Time ( days ) Figure 10 - Maximum crevice pit depth vs. exposure time for alloys evaluated in the outlet ducting Zone F for 30 ...
Page 383
Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing ...
Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry chlorides increasing ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone