Page 84
and Decorative Purposes TABLE 8 : Properties of coatings Specimen Mode Thickness Contact Wear Hardness Resistance Resistance ( Knoop ) ( m2 ) ( mg / rev ) A d.c. 11.5 1.6 6.3 x 103 1.17.1.71 47 % B 11.4 1.7 7.6 x 10-3 p.c. 10/20 0.95 ...
and Decorative Purposes TABLE 8 : Properties of coatings Specimen Mode Thickness Contact Wear Hardness Resistance Resistance ( Knoop ) ( m2 ) ( mg / rev ) A d.c. 11.5 1.6 6.3 x 103 1.17.1.71 47 % B 11.4 1.7 7.6 x 10-3 p.c. 10/20 0.95 ...
Page 165
Lookup Tables This last form of a knowledge base is expected to come into increasing popularity as storage space and ... Certainly we could not initialize such a table by hand , but perhaps with the use of a smarter and slower letter ...
Lookup Tables This last form of a knowledge base is expected to come into increasing popularity as storage space and ... Certainly we could not initialize such a table by hand , but perhaps with the use of a smarter and slower letter ...
Page 373
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy analysis anodic application areas base changes chemical chloride cleaning coatings combination complete composition concentration conclusion containing corrosion Corrosion Control corrosion rate corrosion resistance deposits depth described determine direct effect electrochemical Engineering environment equipment evaluation example expert system factor field function given heat higher HNO3 improve increased industry inhibitor ions Israel knowledge layer limited materials measurements mechanical metal methods NACE obtained operation oxide paint passivation performance plant plating polarization possible potential present problems properties protection Radioactive Tracer REFERENCES Research resistance REVIEWS rules runs rust samples selection sintered slurry solution specific specimens stainless steel Standards stress structure substrate surface Table techniques Technology temperature University welding zirconium Zone