Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 31
Page 403
... element has to possess a high exchange current density for the two cathodic reactions : ( i ) hydrogen evolution ( ii ) oxygen reduction . In addition , the noble alloying element has to be inert in the medium to which it is exposed ...
... element has to possess a high exchange current density for the two cathodic reactions : ( i ) hydrogen evolution ( ii ) oxygen reduction . In addition , the noble alloying element has to be inert in the medium to which it is exposed ...
Page 406
... element , / 15 , 16 / being probably Cu . During the exposure to the 1NH2SO4 environment surface segregation of Cu ... elements / 18 , 19 / . This assumption is confirmed by the open - circuit results and by polarization curves of ...
... element , / 15 , 16 / being probably Cu . During the exposure to the 1NH2SO4 environment surface segregation of Cu ... elements / 18 , 19 / . This assumption is confirmed by the open - circuit results and by polarization curves of ...
Page 408
... element in the present case . Potentiodynamic polarization curves of samples sintered for 2h tested in IN H2SO4 ... elements easily oxidized to form passivation layer . POTENTIAL ESCE . ( MV ) 500 400k 300- 200 1 100H -1000 -200- ( b ) ...
... element in the present case . Potentiodynamic polarization curves of samples sintered for 2h tested in IN H2SO4 ... elements easily oxidized to form passivation layer . POTENTIAL ESCE . ( MV ) 500 400k 300- 200 1 100H -1000 -200- ( b ) ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium