Corrosion Reviews, Volume 7Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 27
Page 321
... corrosion rates in 11 media Corrosion rates vs. total sum of alloying components in Ni based alloys . rather than a controlled laboratory environment . Any changes , even in the physical plant system , affecting temperature , flow path ...
... corrosion rates in 11 media Corrosion rates vs. total sum of alloying components in Ni based alloys . rather than a controlled laboratory environment . Any changes , even in the physical plant system , affecting temperature , flow path ...
Page 375
Corrosion Data for Alloys Evaluated in the Absorber Mixing Chamber Zone B in Runs 5 to 7 Alloy Run 5 Run 5 6 .. Run 5 6 7 317LM TABLE 7 : * Corrosion rates for Runs 6 and 7 were not calculated . Crevice Pit Depth , respectively ...
Corrosion Data for Alloys Evaluated in the Absorber Mixing Chamber Zone B in Runs 5 to 7 Alloy Run 5 Run 5 6 .. Run 5 6 7 317LM TABLE 7 : * Corrosion rates for Runs 6 and 7 were not calculated . Crevice Pit Depth , respectively ...
Page 383
5. CONCLUSIONS 1. Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry ...
5. CONCLUSIONS 1. Increasing the slurry chloride content increased the corrosion rates of alloys SS304 and SS316 in the absorber zone . No significant effect was noted on corrosion rates of alloys G , 904L , 625 and C - 4 with slurry ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium