... bold surface pit penetration , as seen in Figure 3 , which may have galvanically retarded crevice corrosion of the alloy . While the least squares fit line for alloy 625 in Figure 4 indicates increasing severity of crevice attack with ...
... bold surface pit penetration , as seen in Figure 3 , which may have galvanically retarded crevice corrosion of the alloy . While the least squares fit line for alloy 625 in Figure 4 indicates increasing severity of crevice attack with ...
Page 376
... bold surface and crevice pit depth increased with increasing environmental fluoride content . No consistent effect ... bold surface pitting than alloy G - 3 . 3.2 Effect of Exposure Time In run 8 , a 20,000 ppm chloride ( derived from Ca ...
... bold surface and crevice pit depth increased with increasing environmental fluoride content . No consistent effect ... bold surface pitting than alloy G - 3 . 3.2 Effect of Exposure Time In run 8 , a 20,000 ppm chloride ( derived from Ca ...
Page 383
... bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy G , while the other alloys ( except C - 4 ) showed a similar but lower ...
... bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy G , while the other alloys ( except C - 4 ) showed a similar but lower ...
Other editions - View all
Common terms and phrases
acid addition alloy analysis anodic application Artificial Intelligence ASTM Austenitic Austenitic Stainless Steel Bold Surface Pit brazing cathodic cathodic protection chemical chloride chromate coatings composition computerized containing CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS current density database deposits effect electrochemical electronic electroplating environment equipment evaluation example expert system factor fluoride Hastelloy HNO3 hot pressed impellers increased industry inhibitor interface ion implantation ions Israel knowledge base laboratory layer materials selection mechanical metal methods Michael Schorr MYCIN NACE outlet ducting Zone paint parameters passivation phosphate plating polarization curve porosity potentiostat primer Prof properties protection Research Rocchini rules runs Rusted Steel samples Schorr sintered sintered stainless steel slurry soldering solution specimens spraying stainless steel stress corrosion cracking structure substrate Table techniques Technology temperature wear resistance welding zirconium